Super XG No.777 Speed hardening Multi purpose Elastic Adhesive
Shi Min's Super-XG No.777 is a single-component ultra-fast curing elastic adhesive launched by the Japanese CEMEDINE company. Its main component is acrylic-modified silicone resin, and it is an upgraded and improved version of Super X No.8008. It adopts the new concept of "instant elasticity", mainly targeting the demand for short-term positioning bonding. After application, it can be fixed by applying pressure approximately 1-2 minutes later (at 23℃), without the need for mixing or heating. It is very easy to use. The product comes in three colors: white, black, and transparent. The common specification is a 135ml soft tube.
Product Details
Features
Rapid curing: Enables fast formation of bonding strength.
Excellent low-temperature curability: Performs well even in low-temperature environments.
Versatility for bonding a wide range of materials: Applicable to various material types.
High durability: Maintains stable performance under harsh conditions.
Siloxane-free: Does not contain siloxane components.
Applications
Suitable for multi-purpose bonding scenarios that require initial build-up strength (see details below).
Suitable for bonding scenarios that demand durability, such as resistance to thermal cycling.
Supplementary Notes (at 23℃):
After application, with an open time (workable time between application and bonding) of approximately 1 minute, the handling time (time until it can be moved/operated) is about 1–2 minutes.
After application, with an open time of approximately 2 minutes, the handling time is about 30 seconds–1 minute.
| Project | Parameters |
| Product Name | Super-XG No.777 |
| Usage/Characteristics/Advantages | High-speed hardening type |
| Type | Single-component elastic adhesive |
| Main Component | Acrylic modified silicone resin |
| Appearance |
White: White to white-yellow paste; Black: Black paste; Transparent: Light yellow transparent paste |
| Viscosity（Pa·s/23℃） |
White: 82.0; Black: 82.6; Transparent: 76.0 |
| Density（g/cm³） |
White: 1.14; Black: 1.14; Transparent: 1.02 |
| Touch-drying time（23℃） |
White: 2.5 minutes; Black: 2.5 minutes; Transparent: 3.5 minutes |
| Tension shear bonding strength |
White: 3.2 MPa; Black: 3.2 MPa; Transparent: 5.9 MPa |
| T-type peel bonding strength |
White: 3.31 N/mm; Black: 3.31 N/mm; Transparent: 3.08 N/mm |
| Hardness (Shore A) |
White: 58; Black: 58; Transparent: 60 |
| Breaking strength |
White: 3.42 MPa; Black: 3.42 MPa; Transparent: 3.65 MPa |
| Breaking elongation |
White: 120%; Black: 120%; Transparent: 110% |
| Volume resistivity |
White: 3.5×10¹² Ω·cm; Black: 3.3×10¹¹ Ω·cm; Transparent: 2.3×10¹² Ω·cm |
| White: 5.12; Black: 6.30; Transparent: 3.87 |
White: 5.12; Black: 6.30; Transparent: 3.87 |
| Dielectric loss tangent (100Hz) |
White: 0.19; Black: 0.28; Transparent: 0.07 |
| Environmental protection certification | RoHS compliant product, JAIA 4VOC baseline suitable |
| Capacity specification | 135ml/soft tube |
TERADA TERADITE TE-7901 Thermally Conductive Flame-Retardant Two-Component Epoxy Potting Resin
TERADA TERADITE TRU-0252K5 Hard-Type UV-LED Curable Functional Resin
TERADA TERADITE TE-7817 High-Thermal-Conductivity High-Heat-Resistance Flame-Retardant Epoxy Potting Resin
TERADA TERADITE TRU-0250K High-Thixotropy High-Heat-Resistance UV Curable Functional Resin
TERADA TERADITE TE-6430 Thermally Conductive Flame-Retardant Two-Component Epoxy Potting Resin
TERADA TERADITE TRU-0251FR High-Tg Flame-Retardant UV Curable Functional Resin
TERADA TERADITE TE-6010GK5 Low-Chlorine High-Heat-Resistance Two-Component Epoxy Resin
TERADA TERADITE TE-6011K Fast-Curing Two-Component Epoxy Resin for Electronic Insulation & Protection
Shin-Etsu Pure Sealant One-Component Low-Volatility Silicone Sealant for Clean Rooms
TERADA TERADITE TE-6311K8 Low-Specific-Gravity Two-Component Epoxy Resin for Electronic Insulation & Protection
TERADA TERADITE TRU-0260K2 High-Specific-Gravity High-Hardness UV-LED Curable Functional Resin