CEMEDINE Y600H Metal Lock High-Viscosity Second-Generation Acrylic Structural Adhesive
CEMEDINE Y600H is a second-generation acrylic structural adhesive (SGA) in the Metal Lock series. It is the high-viscosity grade in the general-purpose lineup and is designed to provide high toughness, structural bonding strength and rapid room-temperature curing. Both Part A and Part B have a viscosity of approximately 30,000 mPa·s at 23°C, making Y600H suitable for applications where the adhesive must stay in place and resist sagging. The standard mixing ratio is 1:1, with a pot life of approximately 2 minutes at 23°C and a set time of approximately 4 minutes.
Product Details
Product Features
High-Viscosity Grade:Approx. 30,000 mPa·s at 23°C for both parts, providing good non-sag performance.
High Toughness & Structural Strength:Suitable for industrial joints requiring reliable mechanical performance.
Fast Room-Temperature Cure:Approx. 2 min pot life and 4 min set time at 23°C.
1:1 Mixing Ratio:Equal-part mixing for convenient application.
Low Odor:Lower odor than conventional acrylic adhesive systems.
Oil-Tolerant Bonding:Maintains adhesion even on slightly oily surfaces.
Product Applications
Dissimilar Material Bonding:For metal-to-CFRP and other mixed-material assemblies.
Automotive & Vehicle Assembly:Structural bonding of vehicle components.
Sheet Metal Bonding:Bonding steel and other metal sheets.
Steel Furniture:Assembly bonding for office furniture.
Sports Equipment:Assembly applications such as golf clubs.
Industrial Structural Parts:For fast-setting, high-strength industrial assembly.
| Item | CEMEDINE Y600H |
|---|---|
| Product Type | Second-Generation Acrylic Structural Adhesive (SGA) |
| Brand | CEMEDINE |
| Model | Y600H |
| Series | Metal Lock |
| Grade | High-Viscosity Type |
| Main Component | Acrylic Resin |
| Part A Appearance | White |
| Part B Appearance | Gray |
| Part A Viscosity | 30,000 mPa·s at 23°C |
| Part B Viscosity | 30,000 mPa·s at 23°C |
| Mixing Ratio | A:B = 1:1 |
| Pot Life | Approx. 2 min at 23°C |
| Set Time | Approx. 4 min at 23°C |
| Tensile Shear Strength | 19.4 MPa |
| T-Peel Strength | 3.6 N/mm |
| Hardness | Shore D 65 |
| Glass Transition Temperature | 78°C |
| Elastic Modulus | 742 MPa |
| Breaking Strength | 14.0 MPa |
| Elongation at Break | 8% |
CEMEDINE Primer PP7F Primer for Polypropylene (PP)
CEMEDINE PM210 Two-Component Low-Viscosity Flow-Type Modified Silicone Elastic Adhesive
CEMEDINE PM200 Two-Component High-Viscosity Modified Silicone Elastic Adhesive
CEMEDINE PM100 One-Component Modified Silicone Elastic Adhesive
CEMEDINE High-Quick High-Viscosity 5-Minute Epoxy Adhesive
CEMEDINE EP811 One-Part Heat-Curing Epoxy Potting Adhesive
CEMEDINE EP001HT High-Viscosity Flexible Epoxy-Modified Silicone Adhesive