TERADA TERADITE TRU-0250K High-Thixotropy High-Heat-Resistance UV Curable Functional Resin
TERADITE TRU-0250K is a UV-curable functional resin developed by Terada Co., Ltd. It belongs to the TERADITE UV Curable Resin series, which is designed for adhesive and coating applications and emphasizes rapid UV curing, good workability, heat resistance and moisture resistance. TRU-0250K is characterized by High T.I (T.I 3.7). Its viscosity at 25°C is approximately 158,000 mPa·s, providing strong shape retention and making it suitable for dispensing, localized coating and applications where sagging or flow must be minimized. After curing, the material has a Shore D hardness of approximately 86, a Tg of approximately 125°C, and a CTE of approximately 32 ppm/K. The recommended curing condition is 1,500 mJ/cm² using a UV metal-halide lamp. The catalog does not indicate LED-curing compatibility for this grade.
Product Details
Product Features
High Thixotropy: T.I of approximately 3.7 for excellent shape retention
High Viscosity: Approximately 158,000 mPa·s at 25°C
Heat Resistance: Tg of approximately 125°C
High Hardness: Shore D hardness of approximately 86 after curing
Low Thermal Expansion: CTE of approximately 32 ppm/K
Fast UV Curing: UV-curing process helps improve production efficiency
Product Applications
Electronic Components: Bonding, fixing and localized protection of electronic parts
Electrical Assemblies: Structural bonding of electrical modules and components
Precision Components: Suitable for dispensing areas requiring minimal flow
Vertical Applications: Suitable for vertical, edge and localized thick-coating areas
Functional Coating: Protective coating requiring high thixotropy, hardness and heat resistance
Industrial Electronics: Bonding and protection of controllers, modules and industrial electronic devices
| Item | TERADITE TRU-0250K |
|---|---|
| Product Type | UV Curable Functional Resin |
| Series | UV Curable Resin |
| Main Application | Adhesive / Coating |
| Key Characteristic | High Thixotropy |
| Thixotropic Index (T.I) | 3.7 |
| Viscosity at 25°C | 158,000 mPa·s |
| Hardness | Shore D 86 |
| Glass Transition Temperature | 125°C |
| CTE (α1) | 32 ppm/K |
| Shear Bond Strength (AL/AL) | Not Listed |
| Shear Strength after 85°C/85%RH, 1000 h | Not Listed |
| LED Curing | Not Supported / Not Listed |
| Recommended Curing Condition | UV Metal Halide Lamp, 1,500 mJ/cm² |